The waterborne epoxy resin and waterborne curing agent as the film-forming material of zinc phosphate and iron oxide red as anticorrosion pigment composition and two-component waterborne paint. On the surface of steel phosphating, the formation of a special protective layer in the anode range. Has the water resistance, rust resistance and good performance, with excellent adhesion to blasting steel, good matching, can be matched with various anti-corrosion paint or paint. Rapid drying, very low VOC, is an ideal environmental protection anti-corrosion coating.
Suitable for chemical engineering equipment, pipelines, bridges, storage tanks, ships, marine equipment, terminals, locomotives, vehicles, mining equipment, such as steel components to rust and anti-corrosion primer.
Color: iron red or gray
Luster: no light
Solid: = 60%
Theoretical spreading rate: 0.3kg/m2 (dry film thickness of 50 m)
Dry: less than 2H (25 C)
Hard work: less than 24h (25 C)
Fully cured: 7d (25 DEG C)
Flash point: no
Mixing ratio: according to the packaging label
Construction method: spray, brush or roller coating
Thinner: clean water
Aging time: 15min (25 C)
Applicable period: 2 ~ 3H (25 DEG C)
Tool cleaning: clean water
Supporting: completely dry with water or solvent type topcoat.
Sealed in 5 to 35 degrees, cool and dry place, for 6 months.
Note: it is strictly prohibited to contact with oily substances, while the ambient temperature is below 10 DEG C or humidity is greater than 75%, the film drying is very slow, can not be constructed.
Statement: paint many factors in construction directly affects the coating effect and service life, the information and data are based on our experimental testing and actual use of the experience accumulated for the construction, when we do not understand the situation, we can only guarantee the quality of the paint. The above data are subject to change, subject to the company's latest specifications, without prior notice.